特细砂高强混凝土的微观结构测试与研究

doi:10.11835/j.issn.1674-4764.1996.03.012

首页 > 过刊浏览>1996年第18卷第3期 >78. DOI:10.11835/j.issn.1674-4764.1996.03.012

特细砂高强混凝土的微观结构测试与研究
DOI:
                        10.11835/j.issn.1674-4764.1996.03.012
                    
CSTR:
                        [cstr]
                    
作者:
                        
                        
                    
作者单位:
作者简介:
通讯作者:
中图分类号:TU528.31
基金项目:

Experiment And Study On Microstructure of Superfine- sand High Strength Concretes

Author:

Affiliation:

Fund Project:

摘要

图/表

访问统计

参考文献

相似文献

引证文献

资源附件

文章评论

摘要:

本文用细度模数为０．５６的特细砂配制２８天抗压强度达８０ＭＰａ，抗渗透压大于４．０ＭＰａ，收缩徐变小的高强混凝土进行了孔隙结构，水化产物，水泥石有料界面过渡区显微硬度测试和研究。

Abstract:

A high strength concrete with 28 day strength up to 80 MPa from superfine sand with fineness modulus of 0.56 is obtained.It has a permeability resistance of 4.0 MPa and small shrinkage creep.Experiment and study were carried out on its pore structure,hydration products and microhardness of transient area in cement paste and aggregate interface. The essence for high strength of such concrete was revealed.

参考文献

相似文献

引证文献

引用本文

雷映平陈惟时.特细砂高强混凝土的微观结构测试与研究[J].土木与环境工程学报（中英文）,1996,18(3):78-. Lei Yingping. Experiment And Study On Microstructure of Superfine- sand High Strength Concretes[J]. JOURNAL OF CIVIL AND ENVIRONMENTAL ENGINEERING,1996,18(3):78-.10.11835/j. issn.1674-4764.1996.03.012