It is recognized that the scaling failure of nodular iron composite rolls in hot rolling is a problem of fatigue brittle fracture. The temperature field,stress,critical crack size as well as the interior quality of the rolls are presented. The theory of fracture mechanics is used to explain the cause of the scaling failure. At the same time, the way to extend the durability of the rolls is also studied.