Morphologies of precipitation phases along grain boundary of the as-cast Mg-6.0Zn-0.45Zr, Mg-6.0Zn-(1.2Y) and Mg-6.0Zn-0.6Zr-1.0Y alloys are studied by using the methodologies of metallurgical phase analysis, scanning electron microscopy(SEM) analysis and energy diffraction x-ray(EDX) analysis. The experimental result indicates that the main precipitation phases along grain boundary of the as-cast alloys Mg-6.0Zn-0.45Zr is Mg-Zn binary phase. There are two kinds of precipitation phases along grain boundary for Mg-6.0Zn-1.2Y and Mg-6.0Zn-(0.6)Zr-1.0Y alloys. One grew at triangular grain boundary, which is fish-bone -like and contained Mg-Zn binary phase and Mg-Zn-Y ternary phase. The other distributed mainly around the grain, which is net-like and contained Mg-Zn-Y ternary phase. In addition, there are lots of granular phases, extending to the interior of the grain, at the rim of grain boundary phases. Finally, Y can intensively change morphology of precipitation phases along grain boundary of the as-cast Mg-Zn-Zr alloy (ZK60) alloys.