The effect of Ce addition on Ascast microstructures of AZ31 magnesium alloy
Article
Figures
Metrics
Preview PDF
Reference
Related
Cited by
Materials
Abstract:
Various opinions still exist regarding the grain refinement of magnesium alloys resulting from Ce addition. We investigate effect of Ce addition on the ascast microstructures of AZ31 magnesium alloy. The research results indicate that adding from 0.5 wt% to 1.5 wt% Ce to AZ31 magnesium alloy does not effectively refine the alloy grains; instead, the opposite effect results, causing obvious grain coarsening. The coarsening trend is related to the amount of Ce. After adding 0.5 wt% Ce to AZ31 magnesium alloy, the average alloy grain size increases from 60 μm to 164 μm. Furthermore, increasing the amount of Ce added from 0.5 wt% to 1.5 wt% causes the average grain size to decrease gradually. The average grain size of AZ31 magnesium alloy with and additional 1.5 wt% Ce still exceeds that of the AZ31 magnesium alloy without additional Ce, however.