Mg-8Zn-4Al-(0~1)Sr镁合金铸态组织中的第二相研究
作者:
作者单位:

作者简介:

通讯作者:

中图分类号:

TG136

基金项目:

国家自然科学基金资助项目(U1610253,51971053);中央高校基本科研业务费项目(N2002011);辽宁省-沈阳材料科学国家研究中心联合研发基金(2019JH3/30100040)。


The second phases in as-cast Mg-8Zn-4Al-(0-1)Sr magnesium alloys
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    通过扫描电镜观察(SEM)、能谱分析(EDS)、X射线衍射分析(XRD)以及差热分析(DSC)等实验手段,系统地研究了添加微量Sr元素(质量分数0 ~1%)对铸态Mg-8Zn-4Al(ZA84)镁合金组织中的第二相种类的影响,并阐明了第二相形成与演变的内在机理。实验结果表明:未添加Sr元素的铸态Mg-8Zn-4Al合金组织由Q准晶相和少量Mg32(Al,Zn)49相组成。添加Sr元素后,合金铸态组织中均存在Al4Sr和Mg32(Al,Zn)49相;其中Al4Sr相随Sr含量增加而增加,Mg32(Al,Zn)49相随Sr含量增加而减少。在Mg32(Al,Zn)49相中Sr元素以未固溶和固溶两种形式存在,其中未固溶Sr元素的Mg32(Al,Zn)49相具有相对较高的Zn原子浓度和较低的Al原子浓度。相关结果将为第二相析出强化型Mg-8Zn-4Al合金的高强化与耐热化设计提供必要的理论支撑。

    Abstract:

    To systematically investigate the effect of Sr addition on the second phases in the as-cast Mg-8Zn-4Al magnesium alloy and provide the theoretical basis for the design of the Mg-Zn-Al series alloys containing Sr element, the type and formation mechanism of second phases in the ZA84 as-cast magnesium alloys with low Sr mass fractions (0.1%, 0.3%, and 1.0%) were investigated and analyzed by using scanning electron microscope (SEM), energy dispersive spectrometer (EDS), differential scanning calorimetry (DSC), and X-ray diffractometer (XRD). The results indicate that for the ZA84 as-cast alloy without Sr addition, besides the quasicrystal phase (Q), an extra Mg32(Al, Zn)49 phase with a small amount is found to exist in the alloy. With Sr addition, there are Al4Sr and Mg32(Al, Zn)49 phases in the as-cast alloy; the Al4Sr phase increases and Mg32(Al, Zn)49 phase decreases with increase of Sr content. In the Mg32(Al,Zn)49 phases of the as-cast Mg-8Zn-4Al-(0.1-1)Sr magnesium alloys, Sr mainly exists in two forms, i.e. indissolved and dissolved Sr atoms; in the Mg32(Al,Zn)49 phase where Sr atoms are not dissolved, the Zn concentration is relatively high and Al concentration is low. The results provide the necessary theoretical support for the design of reinforced and heat-resistant Mg-8Zn-4Al alloy.

    参考文献
    相似文献
    引证文献
引用本文

吴菊英,李景仁,张晋涛,罗丽,杨明波,吴璐,潘虎成. Mg-8Zn-4Al-(0~1)Sr镁合金铸态组织中的第二相研究[J].重庆大学学报,2021,44(4):117-128.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2020-03-24
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2021-04-20
  • 出版日期: