Ni-Fe双金属纳米颗粒的制备及其性能试验研究
DOI:
作者:
作者单位:

重庆大学

作者简介:

通讯作者:

中图分类号:

基金项目:


Study on Preparation and properties of Ni-Fe bimetallic nanoparticles
Author:
Affiliation:

Chongqing Univisity

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    为制备吸附性与还原性优良的零价铁,试验结合金属修饰与固体负载的两种改性方法,采用电沉积法制备活性炭负载型镍铁双金属颗粒(Ni/Fe-AC BPs)。通过场发射扫描电镜(FESEM)、能谱图(EDS)、比表面积分析仪(BET)进行表征,并以六价铬去除率为其性能评价指标。单因素制备试验结果表明:最优沉积液配比为硫酸铁400g/L,硫酸镍80g/L,硼酸40g/L,硫酸锰60g/L;最佳电沉积条件为电流密度0.45A/cm2,温度40℃,电沉积10min,此条件下,六价铬去除率高达100%。FESEM、EDS及XRD证实了镍铁双金属颗粒制备成功,且所制材料呈絮球状,分散均匀;BET及AC、Fe-AC、Ni/Fe-AC BPs除铬对比试验表明, Ni/Fe-AC BPs的比表面积较AC小47.6%,但除Cr(Ⅵ)率高达100%,而AC吸附率仅5.43%。因此,Ni/Fe-AC BPs具有良好的催化还原性能。

    Abstract:

    To prepare zero-valent iron with excellent adsorptive and reducible properties, activated carbon is used as a load, and modified with metal modification to obtain activated carbon-supported Ni/Fe bimetallic particles by electro-deposition. Ni/Fe-AC BPs were characterized by FESEM, EDS, and BET analyzer, and the Cr(Ⅵ) removal rate was used as the performance evaluation index. The results of single factor preparation test showed that the optimum deposition solution ratio was 400 g/L of ferric sulfate, 80 g/L of nickel sulfate, 40 g/L of boric acid and 60 g/L of manganese sulfate. The optimum electrodeposition conditions were current density of 0.45A/cm2, temperature of 40 C and 10 min of electrodeposition. Under these conditions, the removal rate of hexavalent chromium was as high as 100%. FESEM, EDS and XRD confirmed that the preparation of nickel-iron bimetallic particles was successful, and the prepared materials were flocculent and uniformly dispersed. The comparison tests of BET and AC, Fe-AC, Ni/Fe-AC BPs for chromium removal showed that the specific surface area of Ni/Fe-AC BPs was 47.6% smaller than AC, but the removal rate of Cr (VI) was 100%, while the adsorption rate of AC was only 5.43%. Therefore, Ni/Fe-AC BPs have good catalytic reduction performance.

    参考文献
    相似文献
    引证文献
引用本文
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2018-12-14
  • 最后修改日期:2019-01-17
  • 录用日期:2019-02-14
  • 在线发布日期:
  • 出版日期: